KINETIC STUDY AND MECHANICAL QUALITATIVE CONTROL OF AISI 4140 BORONIZED STEEL FOCUSED ON THE ROLE OF THE AUSTENITIC TRANSFORMATION OF THE SUBSTRATE DURING THE PROCESS
Dimitrios I. Zagkliveris, Olga Valentini I. Tyrilou, Georgios K. Triantafyllidis
Pagini: 279-291
Publicat: 18 Sep 2019
Vizualizări: 2,001
Descărcări: 182
Rezumat: In this study a series of boronizing experiments was performed on AISI 4140 steel’s surface in temperature and time ranges 1073 – 1273 K and 4 – 12 hours, respectively. The well known pack boronizing method was applied and a thick dense, verified with XRD characterization, Fe2B layer was formed, with thickness reaching 160 μm. The material showed a satisfactory response to the boronizing treatment, except for the long-lasting experiments (12 hours), in which the coating was significantly thinner in comparison to the theoretical expectation, due to adsorbed boron depletion. After applying a Fick’s Law-based model and extracting the kinetic parameters, we observed an alteration of the diffusion coefficient of boriding related to austenitizing crystallographic transformation of the ferrous substrate. Additionally, enhancing the results of the kinetic study, an evaluation of the quality of the boride coating was operated via micro-Vickers and Rockwell C (VDI 3198) indentation tests, complemented with optical and SEM imaging. Vickers measurements varied between 1500 HV and 2200 HV. Rockwell C qualification test results were excellent at specific boronizing conditions, proving that boronizing is one of the most advantageous superficially protective techniques for steels.
Cuvinte cheie: coating technology, diffusion, kinetics, mechanical properties, scanning electron microscopy, x-ray diffraction, boriding, steels
Citează acest articol: Dimitrios I. Zagkliveris, Olga Valentini I. Tyrilou, Georgios K. Triantafyllidis. KINETIC STUDY AND MECHANICAL QUALITATIVE CONTROL OF AISI 4140 BORONIZED STEEL FOCUSED ON THE ROLE OF THE AUSTENITIC TRANSFORMATION OF THE SUBSTRATE DURING THE PROCESS. Journal of International Scientific Publications: Materials, Methods & Technologies 13, 279-291 (2019). https://www.scientific-publications.net/en/article/1001902/
Înapoi la cuprinsul volumului
© 2026 The Author(s). This is an open access article distributed under the terms of the
Creative Commons Attribution License https://creativecommons.org/licenses/by/4.0/, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. This permission does not cover any third party copyrighted material which may appear in the work requested.
Disclaimer: The Publisher and/or the editor(s) are not responsible for the statements, opinions, and data contained in any published works. These are solely the views of the individual author(s) and contributor(s). The Publisher and/or the editor(s) disclaim any liability for injury to individuals or property arising from the ideas, methods, instructions, or products mentioned in the content.