SOME PROPERTIES OF NI-ALNI METALLIC-INTERMETALLIC LAMINATE MATERIAL
Burak Besen, Mustafa Kalayci, Tuba Yener, Sakin Zeytin
Pagini: 390-396
Publicat: 1 Jan 2013
Vizualizări: 289
Descărcări: 28
Rezumat: Ni-AlNi metallic-intermetallic laminate (MIL) composites have been fabricated in open atmosphere using commercial purity Ni and Al foils with 250 μm initial thickness. Sintering process has performed at 700ºC under 2 MPa pressure for 5 hrs. Composite consisting of alternating layers of metallic Ni and the intermetallic AlNi have been fabricated by reactive foil sintering in open atmosphere furnace. The aluminum foil was almost consumed by forming a nickel aluminide intermetallic compound. Thus, the final microstructure consists of alternating layers of intermetallic compound and unreacted Ni metal. Microstructure and phase characterization were performed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and x-ray diffractometry (XRD). Hardness values of test samples have also measured as 800 HV by vickers indentation method.
Cuvinte cheie: intermetallic, nickel aluminide, laminate composite, sintering
Citează acest articol: Burak Besen, Mustafa Kalayci, Tuba Yener, Sakin Zeytin. SOME PROPERTIES OF NI-ALNI METALLIC-INTERMETALLIC LAMINATE MATERIAL. Journal of International Scientific Publications: Materials, Methods & Technologies 7, 390-396 (2013). https://www.scientific-publications.net/en/article/1003120/
Înapoi la cuprinsul volumului
© 2026 The Author(s). This is an open access article distributed under the terms of the
Creative Commons Attribution License https://creativecommons.org/licenses/by/4.0/, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. This permission does not cover any third party copyrighted material which may appear in the work requested.
Disclaimer: The Publisher and/or the editor(s) are not responsible for the statements, opinions, and data contained in any published works. These are solely the views of the individual author(s) and contributor(s). The Publisher and/or the editor(s) disclaim any liability for injury to individuals or property arising from the ideas, methods, instructions, or products mentioned in the content.